Calcium formate is a new low-temperature early strength accelerator. For cement, calcium formate can significantly improve the early strength and shorten the setting time. It is widely used in mortar (tile adhesive, cement-based plastering mortar, repair mortar, waterproof mortar) flooring, concrete and other industries.

甲酸鈣即可以加快水泥硬化速度，捉高早期強(qiáng)度，又避免了在冬季或低溫潮濕條件下施工凝結(jié)速度過慢的問題，使水泥產(chǎn)品盡早提高強(qiáng)度投入使用，甲酸鈣對(duì)早期強(qiáng)度貢獻(xiàn)較大。

Calcium formate can not only accelerate the hardening speed of cement and improve the early strength, but also avoid the problem of too slow setting speed during construction in winter or under low temperature and humid conditions, so as to improve the strength of cement products and put them into use as soon as possible. Calcium formate makes a great contribution to the early strength.

在夏季甲酸鈣摻量通常為水泥的0.3％～0.7％，在冬季甲酸鈣的用量應(yīng)隨溫度的下降而增加，一般為0.5％～1％，不宜超過2.5％，針對(duì)干粉砂漿中使用的硅酸鹽水泥早期強(qiáng)度低后期強(qiáng)度高的特點(diǎn)，在產(chǎn)品中適量添加甲酸鈣，對(duì)提高早期強(qiáng)度十分有益。

In summer, the content of calcium formate is usually 0.3% ~ 0.7% of cement, and in winter, the content of calcium formate should increase with the decrease of temperature, generally 0.5% ~ 1%, and should not exceed 2.5%. According to the characteristics of low early strength and high later strength of Portland cement used in dry powder mortar, adding an appropriate amount of calcium formate to the product is very beneficial to improve the early strength.